| 1. | The metallurgical report concluded that the cause was high ph stress corrosion cracking.
|
| 2. | It is highly corrosion resistant, except to stress corrosion cracking.
|
| 3. | Especially the selection of unsuitable stainless steels can cause problems with stress corrosion cracking.
|
| 4. | Analysis of the joint showed traces of chlorine, indicating a stress corrosion cracking failure mode.
|
| 5. | Overaging ( aging beyond the peak strength condition ) improves resistance to stress corrosion cracking.
|
| 6. | He proposed a mechanism of stress corrosion cracking
|
| 7. | That failure was attributed to stress corrosion cracking.
|
| 8. | The reason for the failures was stress corrosion cracking of metal fastening components made of stainless steel.
|
| 9. | The cause was stress corrosion cracking.
|
| 10. | Some times these tubes are affected by stress corrosion cracking, if original stress is not fully relieved during manufacture.
|